Author | Tay, A.A.O. Lin, T.Y. |
Copyright Year | 1998 |
Description | Author affiliation: Centre for IC Failure Anal. & Reliability, Nat. Univ. of Singapore, Singapore (Tay, A.A.O.) |
Abstract | Very small defects may exist at interfaces in IC packages due to random factors, manufacturing faults or contamination. During solder reflow, these defects give rise to stress concentrations due to thermal mismatch between the materials forming the interface and to the development of hygrostresses from moisture absorption in the plastic encapsulant. In this paper, the mechanics of interfacial delamination will be discussed and a methodology presented for analysing moisture-induced delamination growth during solder reflow. This paper also describes an experimental study which verified the methodology. In this experimental study, plastic packages which were fabricated with a known internal delamination, were divided into 3 groups and subjected to 3 different levels of moisture preconditioning, namely fully dry, 85/spl deg/C/60%RH and 85/spl deg/C/85%RH. Packages from each group were then subjected to oven temperatures varying from 180/spl deg/C to 230/spl deg/C in increments of 5/spl deg/C. Examining the specimens using a scanning acoustic microscope, the temperature at which delamination propagation occurred was determined and compared with that predicted using mixed-mode interfacial delamination mechanics. Generally good agreement was obtained. The growth of the delamination could be explained in terms of the variation of hygrothermal stress intensity factor and interface toughness with crack length. |
Starting Page | 371 |
Ending Page | 378 |
File Size | 914918 |
Page Count | 8 |
File Format | |
ISBN | 0780345266 |
ISSN | 05695503 |
DOI | 10.1109/ECTC.1998.678720 |
Language | English |
Publisher | Institute of Electrical and Electronics Engineers, Inc. (IEEE) |
Publisher Date | 1998-05-25 |
Publisher Place | USA |
Access Restriction | Subscribed |
Rights Holder | Institute of Electrical and Electronics Engineers, Inc. (IEEE) |
Subject Keyword | Delamination Thermal stresses Moisture Temperature Plastic integrated circuit packaging Manufacturing Contamination Absorption Plastic packaging Ovens |
Content Type | Text |
Resource Type | Article |
Subject | Electronic, Optical and Magnetic Materials Electrical and Electronic Engineering |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
Sl. | Authority | Responsibilities | Communication Details |
---|---|---|---|
1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
7 | National Digital Library of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
Loading...
|