Author | Jin-Rong Cheng Cross, L.E. |
Copyright Year | 2003 |
Description | Author affiliation: Mater. Res. Inst., Pennsylvania State Univ., University Park, PA, USA (Jin-Rong Cheng; Cross, L.E.) |
Abstract | Crystalline solutions of (1-x)(Bi,La) (Ga,Fe)O/sub 3/-xPbTiO/sub 3/ (BLGF-PT) have been developed using conventional mixed oxide ceramic processing. An attractive feature is that BLGF-PT has electrical resistivity up to 10/sup 13/ /spl Omega//spl middot/cm at room temperatures. The MPB of (1-x)BLGF-xPT was shifted to higher x content with increasing La concentration. The La substituent was also found to decrease the ferroelectric coercive field, resulting in significantly dielectric and piezoelectric properties. The dielectric constant K and piezoelectric d/sub 33/ constant of 1760 and 295 pC/N have been achieved for BLGF-PT with La-20 at% and x=0.43, a composition in the vicinity of MPB. BGF-0.3PT (La-0, x=0.3) exhibited great remnant polarization Pr and strain of 67 /spl mu/C/cm/sup 2/ and 0.4% respectively, under an electric field of 150 kV/cm. Our results clearly demonstrate that BLGF-PT is competitive and alternative piezoelectric materials to conventional Pb(Zr,Ti)O/sub 3/ (PZT) ceramics, served as piezoelectric and high power components, but in significantly lead reduced forms. |
Starting Page | 354 |
Ending Page | 357 |
File Size | 328893 |
Page Count | 4 |
File Format | |
ISBN | 0780379225 |
DOI | 10.1109/ULTSYM.2003.1293421 |
Language | English |
Publisher | Institute of Electrical and Electronics Engineers, Inc. (IEEE) |
Publisher Date | 2003-10-05 |
Publisher Place | USA |
Access Restriction | Subscribed |
Rights Holder | Institute of Electrical and Electronics Engineers, Inc. (IEEE) |
Subject Keyword | Lanthanum Ceramics Crystallization Electric resistance Temperature Ferroelectric materials Dielectric constant Piezoelectric polarization Capacitive sensors Piezoelectric materials |
Content Type | Text |
Resource Type | Article |
National Digital Library of India (NDLI) is a virtual repository of learning resources which is not just a repository with search/browse facilities but provides a host of services for the learner community. It is sponsored and mentored by Ministry of Education, Government of India, through its National Mission on Education through Information and Communication Technology (NMEICT). Filtered and federated searching is employed to facilitate focused searching so that learners can find the right resource with least effort and in minimum time. NDLI provides user group-specific services such as Examination Preparatory for School and College students and job aspirants. Services for Researchers and general learners are also provided. NDLI is designed to hold content of any language and provides interface support for 10 most widely used Indian languages. It is built to provide support for all academic levels including researchers and life-long learners, all disciplines, all popular forms of access devices and differently-abled learners. It is designed to enable people to learn and prepare from best practices from all over the world and to facilitate researchers to perform inter-linked exploration from multiple sources. It is developed, operated and maintained from Indian Institute of Technology Kharagpur.
Learn more about this project from here.
NDLI is a conglomeration of freely available or institutionally contributed or donated or publisher managed contents. Almost all these contents are hosted and accessed from respective sources. The responsibility for authenticity, relevance, completeness, accuracy, reliability and suitability of these contents rests with the respective organization and NDLI has no responsibility or liability for these. Every effort is made to keep the NDLI portal up and running smoothly unless there are some unavoidable technical issues.
Ministry of Education, through its National Mission on Education through Information and Communication Technology (NMEICT), has sponsored and funded the National Digital Library of India (NDLI) project.
Sl. | Authority | Responsibilities | Communication Details |
---|---|---|---|
1 | Ministry of Education (GoI), Department of Higher Education |
Sanctioning Authority | https://www.education.gov.in/ict-initiatives |
2 | Indian Institute of Technology Kharagpur | Host Institute of the Project: The host institute of the project is responsible for providing infrastructure support and hosting the project | https://www.iitkgp.ac.in |
3 | National Digital Library of India Office, Indian Institute of Technology Kharagpur | The administrative and infrastructural headquarters of the project | Dr. B. Sutradhar bsutra@ndl.gov.in |
4 | Project PI / Joint PI | Principal Investigator and Joint Principal Investigators of the project |
Dr. B. Sutradhar bsutra@ndl.gov.in Prof. Saswat Chakrabarti will be added soon |
5 | Website/Portal (Helpdesk) | Queries regarding NDLI and its services | support@ndl.gov.in |
6 | Contents and Copyright Issues | Queries related to content curation and copyright issues | content@ndl.gov.in |
7 | National Digital Libarray of India Club (NDLI Club) | Queries related to NDLI Club formation, support, user awareness program, seminar/symposium, collaboration, social media, promotion, and outreach | clubsupport@ndl.gov.in |
8 | Digital Preservation Centre (DPC) | Assistance with digitizing and archiving copyright-free printed books | dpc@ndl.gov.in |
9 | IDR Setup or Support | Queries related to establishment and support of Institutional Digital Repository (IDR) and IDR workshops | idr@ndl.gov.in |
Loading...
|